CW611N
Brass is essentially copper alloyed with zinc. It is strong but easy to form, stamp or draw which make it a common choice for a broad spectrum of applications. By varying the amount of zinc content it is possible to achieve a variety of characteristics including different levels of corrosion resistance, ductility and suitability for machining.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
|---|---|---|
| Cu | 59.00 | 60.00 |
| Pb | 0.80 | 1.60 |
| Sn | - | 0.20 |
| Fe | - | 0.20 |
| Al | - | 0.05 |
| Ni | - | 0.30 |
| Total Others | - | 0.20 |
| Zn | Remainder | |
Mechanical Properties According To EN12164 (As Per Temper R410)
| Range (mm) | From | To | UTS Min (N/mm²) | UTS Max (N/mm²) | PS Min (N/mm²) | Elongation Min (%) | Hardness Min | Hardness Max | |
|---|---|---|---|---|---|---|---|---|---|
| Round (Dia) | 2 | 40 | 410 | - | 230 | 12 | - | - | |
| Hex (A/F) | 2 | 35 | 410 | - | 230 | 12 | - | - | |
| Square (A/F) | 2 | 35 | 410 | - | 230 | 12 | - | - | |
| PHYSICAL PROPERTIES | |
|---|---|
| Melting Point – Liquidus °F | 1650 |
| Melting Point – Solidus °F | 1630 |
| Density lb/cu in. at 68°F | 0.304 |
| Specific Gravity | 8.41 |
| Electrical Conductivity % IACS at 68°F | 28 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68°F | 71 |
| Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) | 11.6 |
| Specific Heat Capacity Btu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
| FABRICATION PROPERTIES | |
|---|---|
| Technique | Suitability |
| Soldering | Excellent |
| Brazing | Good |
| Oxyacetylene Welding | Fair |
| Gas Shielded Arc Welding | Fair |
| Coated Metal Arc Welding | Not Recommended |
| Spot Weld | Not Recommended |
| Seam Weld | Not Recommended |
| Butt Weld | Fair |
| Capacity for Being Cold Worked | Fair |
| Capacity for Being Hot Formed | Excellent |
| Machinability Rating | 60 |
TYPICAL USES
- Builders Hardware
- Consumer
- Building
- Industrial