CW622N
CW622N Leaded brass, is a significantly improved form of 60/40 brass, it is used in the mass production of brass components where maximum output and longest tool life are required, and where no further cold forming after machining is required.
CHEMICAL COMPOSITION
| Elements | Min (%) | Max (%) |
|---|---|---|
| Cu | 55.00 | 57.00 |
| Pb | 0.80 | 1.60 |
| Sn | - | 0.30 |
| Fe | - | 0.30 |
| Al | 0.05 | 0.50 |
| Ni | - | 0.30 |
| Total Others | - | 0.20 |
| Zn | Remainder | |
Mechanical Properties According To EN12167
No Mechanical properties for this alloy. Mechanical properties as agreed between punchers and supplier.| PHYSICAL PROPERTIES | |
|---|---|
| Electrical conductivity %IACS | 25 |
| Thermal conductivity W/(m·K) | 113 |
| Thermal expansion coefficient (0–300 °C) | 10⁻⁶ /K 21.40 |
| Density | 8.46 g/cm3 |
| Modulus of elasticity | 96 Gpa |
| FABRICATION PROPERTIES | |
|---|---|
| Technique | Suitability |
| Machinability (CuZn39Pb3 = 100 %) | 80% |
| Capacity for Being Cold Worked | Poor |
| Capacity for Being Hot Worked | Excellent |
| Resistance welding (butt weld) | Fair |
| Inert gas shielded arc welding | Poor |
| Gas welding | Poor |
| Hard soldering | Fair |
| Soft soldering | Excellent |
| Melting range | 880–895 °C |
| Hot working | 650–800 °C |
| Soft annealing (1–3 h) | 450–600 °C |
| Thermal stress relieving (1–3 h) | 200–300 °C |